PPPL-4787

Plasma Facing Surface Composition During NSTX Li Experiments

Authors: C.H. Skinner, R. Sullenberger, B.E. Koel, M.A. Jaworski and H.W. Kugel

Abstract:
Lithium conditioned plasma facing surfaces have lowered recycling and enhanced plasma performance on many fusion devices. However, the nature of the plasma-lithium surface interaction has been obscured by the difficulty of in-tokamak surface analysis. We report laboratory studies of the chemical composition of lithium surfaces exposed to typical residual gases found in tokamaks. Solid lithium and a molybdenum alloy (TZM) coated with lithium has been examined using x-ray photoelectron spectroscopy, temperature programmed desorption, and Auger electron spectroscopy both in ultrahigh vacuum conditions and after exposure to trace gases. Lithium surfaces near room temperature were oxidized after exposure to 1-2 Langmuirs of oxygen or water vapor. The oxidation rate by carbon monoxide was four times less. Lithiated PFC surfaces in tokamaks will be oxidized in about 100 s depending on the tokamak vacuum conditions.
__________________________________________________

Submitted to: Journal of Nuclear Materials (May 2012)

__________________________________________________

Download PPPL-4787 (pdf 1.4 MB 15 pp)
__________________________________________________